The effect of Si content in welding wires on th arc stability was investigate, in the region of short circuit transfer and spray transfer. In the region of short circuit transfer, with increasing Si content, average arcing time and average short circuit time were increased. Therefore, droplet transfer frequency was decreased, due to the increase of arcing time and peak current at the moment of arc-reiginition was increased, due to the increase of short circuit time. In the region of spray transfer, the fluctuations of arc current and arc voltage was the most stable in wire with Si content of about 00.60 wt.%.