Removal teals of Soxmox were performed using low density ceramic filters doped with various catalysts. Disc type (50 mmO.Dx10 mmt) low density ceramic filters were doped with three different catalysts such as Cu to remove SOx and NOx, and Mn and Co to remove NOx. The air permeabilities and specific surface areas were 40~50cc/min.cm2.cmH2O and 4.1~8.88 m2/g, respectively. Also, the peak pore sizes of catalyst support were 3~5nm. Tests were focused to search optimum operating temperatures for different catalysts. It was found that as the CuO content increases, SOx removal efficiency was increased. NOx removal efficiencies for Mn, Cu and Co, were 85% at 30$0^{circ}C$, 90% at 40$0^{circ}C$ and 90% at 45$0^{circ}C$, respectively.