Fly ashes mixed with clay as 70:30 weight percent were sintered by microwave energy and a 2.45 Ghz kitchen model microwave oven was used. Samples were sintered at $1,150^{circ}C$ and kept at that temperature up to 50 minutes by 10 minutes intervals. Microstructures were taken by Scanning Electron Microscope (SEM) and Energy Dispersive Spectrometry (EDS) analysis of a raw fly ash was taken. X-ray diffraction analysis was done, and compressive strengths and apparent densities were measured. Pore sizes of the samples became smaller as time passed by, but compressive strengths and apparent densities did not change much. Numerical analysis on the microwave heated system was carried out in order to figure out heat transfer phenomena in the cavity.