$BaTiO_3$ fine particles were prepared by hydrothermal process from titanium tetra-isoproproxide ($Ti(OiPr)_4$) and barium hexa-hydroxide ($Ba(OH)_2{cdot}8H_2O$) as raw materials. The fine particles were obtained at the temperature range of 160 to $185^{circ}C$. The properties of $BaTiO_3$ particles were studied as a function of various parameters such as reaction temperature, reaction time and Ba/Ti ratio, etc. The average particle size of $BaTiO_3$ increased with increasing reaction temperature and time. After hydrothermal treatment at $170^{circ}C$ for 8 h, the average particle size of $BaTiO_3$ was about 30 nm and the particle size distribution was narrow.