The effects of solvents (DMAc, NMP, 1,4-dioxane) and nonsolvents ($H_2O$, Methanol, n-hexane) on the morphology of 6FDA-p-TeMPD polyimide membrane, prepared by the wet phase inversion method, were studied. In the polymer/solvent/nonsolvent ternary system, the binodal curve, the coagulation value and the relative light transmission were measured, and the solubility parameter difference was calculated. The onset state and rate of liquid-liquid alemixing were predicted and the morphology of membrane was analyzed. It is found that the finger-like pores are formed within discontinuous polymer nodules when the binoclal curve is close to the polymer-solvent (P-S) axis, the coagulation value is small, the reduction of light transmission is easy to occur and the order of solubility parameter difference ($Delta delta_{i-j}$) is $Delta delta_{S-NS} > Delta delta_{P-NS} > Delta delta_{P-S}$. The dense skin with small nodules and the sponge type sublayer with macrovoid are formed in the case that the binodal curve is distant from the P-S axis, the onset time of liquid-liquid demixing is long and the order of $Delta delta_{i-j}$ is $Delta delta_{P-NS} >(Delta delta_{S-NS} < > Delta delta_{P-S})$. The thick layer of fine nodule coagulation and loosely grown sublayer of nodules appear when the binodal curve is distant from the P-S axis, the onset time of liquid-liquid demixing is very long and the order of $Delta delta_{i-j}$가 $Delta delta_{S-NS} > (Delta delta_{P-NS}$lessgtr$ > (Delta delta_{P-NS} < >)Delta delta_{P-S}$</TEX> ).