Unite cell of soid oxide fuel cell (SOFC) that consists of a dense yttria-stabilized zirconia(YSZ) electrolyte a porous nickel-YSZ cermet anode and a porous strontium- doped lanthanum manganate(LSM) cathod was fabricated from using pore former through co-firing technique. Initial sintering shrinkage rates of each layer were identified for fabricating SOFC. Heterogenous sintering was very effective in tailoring shrinkage rate for three layers. The powder tailoring necessary for shrinkage rate matching are as follows ; electrolyte of 60% TZ8YS/ 40% TZ8Y mixture anode of 51wt% NiO/49 wt% (70wt% TZ8YS/30 wt% UT ZrO2) mixture and cathode of 80% LSM/20% UT ZrO2 mixture . The overall sintering shrinkage rate differences of three layers using these compositions were maintained in a few percent.