The effect of epoxy resin on the water stability of HAC/PVA based MDF cement composite were stu-died through the three different forming methods calendering extruding and warm pressing. In prexing step the epoxy resin was added in 5-15wt% of cement weight. The 3-point flexural strength of each dry and wet specimen which were immersed in water during 3. 7, 14 days was estmated and the mi-crostructural change of epoxy resin-added MDF cement composite due to water immersion was charac-terized by scanning electron microscopy. As the addition amount of epoxy resin the im-provement of water stability of MDF cement composite was achieved in most case. Especially through the warm press forming method the effectiveness of epoxy resin addition to the water stability was enhanced. When the epoxy resin was added by 5wt% to 7wt% the optimum flexural strength and water stability