The effect of each factor on the porosity and mean pore size of cordierite(2Mg$.$2{{{{ {Al}_{2 } {O }_{3 } }}$.$5{{{{ {SiO}_{2 } }}) ceram-ics which have been mainly used for hot gas filter was investigated by using orthogonal array. The poros-ity was observed to increase with the content of graphite added as pore-forming material and decrease with increasing talc size. The effects of the other factors the graphite size sintering temperature and hold-ing time at sintering temperature were observed to be small relatively. In case of mean pore size the ef-fect of talc size on the mean pore size of cordierity was investigated to be the largest. The mean pore size was observed to increase with increasing talc size.