This experiment is third study concerning BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} (Ln=Sm, Nd, Pr, La..) system which is known to show a high dielectric constant and Q value in microwave dielectric materials. The process of cry-stallization and the microwave dielectric properties of the specimens sintered at 1220-140$0^{circ}C$ for 2 hr was investigated in the BaO-(Na,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} as well as BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system. The single phase BaPr2Ti5O14 and Ba(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}Ti5O14 was finally formed from the Pr2Ti2O7 (Nd, Pr)2Ti2O7 as a secondary phase in the BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} and BaO-(Nd, {{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system respectively The dielectric constant of the specimens sint-ered at 1280~131$0^{circ}C$ showed the maximum value as 105(BaO-{{{{ { { Pr}_{ 2} O}_{3 } }}-{{{{ { TiO}_{2 } }} system) and 88 (BaO-(Nd,{{{{ { { Pr})_{2 }O }_{3 } }}-{{{{ { TiO}_{2 } }} system) and the Q values of them showed higher value than 1800 which are due to the maximum den-sity. However the dielectric properties of the specimens sintered at higher temperature than 131$0^{circ}C$ were reduced due to the increases of pore which were resulted from the sudden grain growth.