The BaTiO3 powders extensively used as MLCC (Multilayer ceramic capacitor) in electronic ceramic in-dustry were synthesized by GNP (Glycine-Nitrate process) The powders were prepared using carbonate and alkoxide as starting materials and nitric acid was used as a solvent for starting materials as well as an oxidant for combustion. The BaTiO3 powders were synthesized using different amounts of glycine as a fuel for combustion. The characteristics of synthesized powders were examined with helium pycnometer X-ray diffraction(XRD) Brunauer-Emmett-Teller with N2 adsorption and scanning electron microscopy(SEM). It was found that single phase BaTiO3 could be formed when the as-synthesized powders were heat-treated at 100$0^{circ}C$ When the glycine/cation molar ratio was 1,2 specific surface area was 24m2/g