Electrodes using for the anode electrode of direct methanol fuel cell with Pt/C and Pt/Ru/C catalyst were prepared and characterized by SEM, TEM, thermal analysis and electrochemical analysis. The half cell tests were carried out with 1 M $H_2SO_4$ electrolyte and 1 M $CH_3OH$ in order to evaluate the electrode performance. The employed electrochemical methods were cyclic vol-tammetry and potentiodynamic polarization experiments. It was found that 20 w% polytetrafluoroethylene (PTFE) content in catalyst showed the best performance due to the best platinum utilization on PTFE-containing catalyst layer. It was found that Pt/Ru/C binary catalyst inhibited the poisoning of anode electrode showing improved performance compared to the Pt/C catalyst by the adsorption of oxygen containing species on the electrode surface at same time. The apparent activation energy for methanol oxidation on the Pt/Ru/C and Pt/C catalyst layer was 11.60 kJ/mol and 26.85 kJ/mol, respectively.