Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environments and in the air. These experiments were done to investigate the corrosion fatigue crack propagation behavior, the variation of aspect ratio for part through crack and electro-chemical characteristics of the metal. The main results obtained are as follows ; 1. Comparing the same surface crack length with the crack depth, the crack depth toward the thickness of specimen in air propagated faster than that in corrosion environment. 2. The aspect variation of the half elliptical crack can be estimated as following equation; b/a=i-jb/t where a : surface crack length, b : crack depth, t : specimen thickness, i,j : experimental constants but the slope j is decreased as specific resistance decreases. 3. As the specific resistance of corrosion environment decrease or the corrosion fatigue crack propagates, the corrosion potential become less noble.