Cotton fabrics were finished with mixture of BTCA(1,2,3,4,-butanetetracarboxylic acid) and polyalkyleneoxide-modified amino-functional silicone by pad-dry-cure process to achieve better DP performance with a higher retention of physical properties as compared to those of finished with BTCA alone. The results indicated that BTCA improved the wrinkle recovery but reduced significantly the tensile and tear strength of the treated fabrics. Whereas silicone imparted a lower wrinkle recovery, a lower loss of tensile strength than BTCA, in addition improved considerably the tear strength owing to reduction in inter-fiber and/or inter-yarn frictional forces. The concentration and curing temperature needed to enhance physical properties were as follows; for BTCA treatments 6%, at 18$0^{circ}C$, for silicone treatments 1% at 14$0^{circ}C$. This optimum concentration of silicone was observed by using the mixture of BTCA and silicone. The wrinkle recovery and DP rating of cotton fabrics treated with mixture of 4% BTCA and 1% silicone at a curing temperature of 17$0^{circ}C$ was similar to those of treated with 6% BTCA at a curing temperature of 18$0^{circ}C$, and other performance properties observed were; an increase in tensile strength, extension, toughness, abrasion resistance and moisture regain due to the reduction of BTCA concentration and curing temperature, futhermore an improvement in bending and surface properties due to the lubricating effect of silicone. On the other hand 1% aqueous silicone solution showed the lowest surface tension. Such nonionic surface activity resulted in a more uniform and rapid deposition of BTCA on the fiber or fabric.