The ultraviolet(UV)-curable materials wildly have been used as a ink and coating materials. A according to measure UV polymerization phase separation of acryl groups 2,3,4-functional monomer, a few experiments were performed gel fraction, dynamic viscosity of alkyd resin blend system. Dependence of photoiniator concentration and various monomer, alkyd resin content investigated structural changes of films cured by UV irradiation. Curing rate measured UV irradiation under $25^{circ}C$, cell gap 7cm and film thickness 100${mu}{ extrm}{m}$. In results, it was through that the viscoelastic properties of films cured with increasing the ratios of monomer/alkydresin contents are network polymer in properties such as viscoelasticity.