The exchange anisotropy between NiO antiferromagnetic layer and NiFe ferromagnetic layer has been investigated in NiFe(10 nm)/NiO(60 nm) formed by magnetron sputtering. The NiO films were sputtered from nickel oxide using R. F. poser and NiFe, Ta were deposited using D. C. power under Ar atmosphere. Above all. we studied the exchange anisotropy of Ni-Fe/NiO bilayer, and focused especially on the effect of NiO depostion condition. Our experimental data showed that the dominant factor for determining the exchange anisotropy properties was the Ar pressure during NiO deposition. The better exchange anisotropy properties were found when the NiO film was deposited at low Ar pressure probably due to the flatten interface and the epitaxial tendency of NiO grains and NiFe grains. However, as Ar pressure increased, interfacial diffusion at NiFe/NiO interface and oxygen content of NiO film increase, and consequently reduced the exchange anisotropy. We concluded that the flatten interface and relatively low oxygen content of NiO layer are dominant factors for the enhancement of the exchange anisotropy in NiFe/NiO bilayer.