High aspect ratio microstructures were fabricated by photolithography. The material for the microstructure was photosensitive glass which has good mechanical and electrical insulation properties. The photosensitive glass was exposed to ultraviolet light at 312nm through a chromium mask in which the structures are drawn. After heat treatment process over $500^{circ}C$, the photosensitive glass was etched in a 10% hydrofluoric acid solution with ultrasonic conditions. Final dimension of the micro-framework was greatly dependent on the thickness of photosensitive glass, mask pattern, ultraviolet light exposure and etching conditions. The maximum aspect ratio of the micro-framework obtained from this work was over 30.