NiCrAlY/YSZ(8wt%$Y_2O_3-ZrO_2$) functionally graded thermal barrier coating (FGC) layers on a Co-base superalloy (HAYNESS 188) substrate were fabstrate were fabicated using Ar shielded single torch air plasma spraying method. Functional grading with the stepwise compositional change throughout layer thickness. Microstructural observation trvealed a successful fabrication of NiCrAlY/YSZ FGC. From the results of the curvature measurement, adhesive strength measurement and thermal shock test for the FGC, it was concluded that the optimum conditions of functionally graded coating layer thinkness and compositional pattern exit to enhance the properties of FGC, which is closely related to the internal residual stess distribution witin it.