In this stydy, submicron shallow trenches applied to STI(shallow tench isolation) were etched using inductively coupled $CI_2$/HBr and $CI_2/N_2$plasmas and the physical and electrical defects remaining on the etched silicon trench surfaces and the effects of various annealing and oxidation on the removal of the defects were studied. Using high resolution electron microscopy(HRTEM), Physical defects were investigated on the silicon trench surfaces etched in both 90%$CI_2$/ 10%$N_2$ and 50%$CI_2$/50%HBr. Among the areas in the tench such as trench bottom, bottom edge, and sidewall, the most dense defects were found near the trench bottom edge, and the least dense defects were found near the trench bottom edge, and least dense defects compared to that etched with ment as well as hydrogen permeation. Thermal oxidation of 200$AA$ atthe temperature up to $1100^{circ}C$apprars not to remove the defects formed on the etched silicon trenches for both of the etch conditions. To remove the physicall defects, an annealing treatment at the temperature high than $1000^{circ}C$ in N for30minutes was required. Electrical defects measured using a capacitance-voltage technique showed the reduction of the defects with increasing annealing temperature, and the trends were similar to the results on the physical defects obtained using transmission electron microscopy.