The microstructures and mechanical properties of submicron WC-Co cemented carbides were investigated in relation to cobalt content. To inhibit the WC grain growth during sintering, VC was added as a inhibitor in each alloy with 3 mass% to the cobalt content. The WC-(5, 8, 10, 15, 20) mass% Co compacts were sintered at $1400^{circ}C$ for 30 min in vacuum. Some of WC-(5, 8, 10) mass% Co sintered compacts were HIPed with 120 atm at 130$0^{circ}C$ for 1 hr. The shrinkages of all HIPed alloys were increased without depending on the cobalt contents and the sintered densities of them. The relative densities of the alloys were increased with the cobalt content and HIPing. The less the cobalt content, the larger the WC grain. Many contiguities of WC grains were found in WC-5 mass% Co alloy. The sizes and numbers of pores in the alloys were decreased by HIPing. And also the strength and the hardness of each alloy were increased. The maximum hardness was about 18.95 GPa in the WC-5 mass% Co alloy HIPed and the maximum transverse-rupture strength (T.R.S.) 3.2 GPa in the WC-20 mass% Co alloy sintered.