The purpose of this study was to investigate the effect of alkali treatment on EG solution of polyester/silk union cloth(P/S cloth) . Tensile strength, moisture regain, crease resistance, and reduction ratio of the treated P/S cloth were measured. The results of this study were as follows ： 1) The weight loss of P/S cloth treated with EG solution was three times higher than those of P/S cloth treated with $H_2O$. The weight loss of P/S cloth was increased greatly with increasing concentration of NaOH, temperature, and time. Favorable weight reduction of treating condition could be obtained when lower concentration of NaOH was used with longer time. 2) If it was added $H_2O$ on EG solution, weight loss of polyester increased, while those of silk decreased. In addition, decreasing ratio of tensile strength warp direction (polyester) was lower, while those of weft direction(silk) was higher. 3) Moisture regain of P/S cloth treated with EG solution increased with weight loss up to 10% . Crease resistance of P/S cloth was the highest at weight loss of 10~15%.