The purpose of this experimental study was to investigate the effects of vulcanization condition on the properties of reinforced rubbers. Rubber reinforcing ability of carbon black was more efficient than other fillers, but tensile properties were not affected by vulcanization condition while vulcanization condition affected the physical properties of rubber compounds with silica and silane treated slica. It was found that silica and silane treated silica filled rubber compounds showed good dynamic properties, rebound, heat build-up, 0 and $60^{circ}C$ tan $delta$ compared with carbon black filled rubber compounds. Carbon black filled rubber compounds were higher than silica and silane treated silica filled rubber compounds in total crosslinking density by vulcanization condition. By analysis of crosslinking type, polysulfide crosslinking was the highest in the carbon black filled rubber compounds with decreasing the ratio of sulfur to accelerator, monosulfide crosslinking was the highest in the silane treated silica filled compounds with in-creasing the ratio of sulfur to accelerator.