In this study, the J-Resistance Curve and material tearing modulus of SA508-C3 steel, which is one of the used nuclear pressure vessel steel, are measured ar room temperature, $200^{circ}C$ and $300^{circ}C$ according to load ratio analysis and ASTM E813, ASTM E1152, respectively. It is observed that J-R curve and Tmat value decrease as the temperature level increase. Applicability of $T_j$ proposed by Paris et al as instability parameter for ductile material is investigated. It is concluded that results are the $T_j$ parameter may be used as a crack instability parameter.