It is well known for 410L ferritic stainless steel powder to applicate a sensor ring in anti-lock brake system of automobile, several studies, because of its excellent magnetic properties. This study was carried out to investigate the magnetic properties such as the maximum magnetic induction, coercivity and maximum permeability of the materials with functions of sintering density, time and temperature, and concluded as follows: 1. Sintering under the circumstances of Ar gas and the temperature of $1250^{circ}C$ for 60min, showed that nitrogen was increased, whereas carbon and oxygen decreased in quantities. 2. Both maximum magnetic induction value of 4700Gauss and permeability of 200 were obtained at the maximum sintering density of $6.89g/cm^2$. Here, the properties showed a linear increasement with increasing the sintering density. 3. Coercivity sharply decreased with incresing the sintering density and reached to 7.6Oe at the maximum sintering density of $6.89g/cm^2$.