This study helps to clarify conflicting reports by comparing the physical properties and accuracy of complete denture processed by the pack and press technique, continuous- pressure injection technique(SR-Ivocap system) and Mark press technique. The 6 different specimens have been evaluated using the SEM, Impact test, DSC (Differential Scanning Calorimetry) and DMTA (Dynamic Mechanical Thermal Analysis). Each sample was made of SR-Ivocap resin and QC-20 resin by different processing methods. The results were as follows ; 1. As the result of the observation on the fracture surface of resin by use of SEM, sample SR-Ivocap resin cured by continuous pressure injection method showed the most homogeneous structure. This is why molecules in SR-Ivocap resin have no orientation. 2. As the result of the Impact test in order to measure the deformity, fracture energy and impact resistance of resin, the samples with QC-20 acrylic resin and SR-Ivocap resin cured by continuous pressure injection method were exellent. 3. In consequence of measuring ${alpha}$-glass transition temperature by use of DSC on the basis of temperature change, the glass transition temperatures of sample QC-20 resin cured by pack and press method and sample SR-Ivocap resin cured by continuous pressure injection method were very similar. Thus volumetric stability could not be evaluated only by glass transition temperature. 4. In comparing volumetric stability data by DMTA, the glass transition temperature(Tg) showed $137.88^{circ}C$ at sample QC-20 resin cured by pack and press method and $139.78^{circ}C$ at sample SR-Ivocap resin cured by continuous pressure injection method. Therefore sample SR-Ivocap resin cured by continuous pressure injection method seems to be superior to sample QC-20 resin cured by pack and press method in the dimensional stability at high temperature. 5. In comparing storage modulus data by DMTA, the storage modulus of sample SR-Ivocap resin cured by continuous pressure injection method was higher than that of sample QC-20 resin cured by pack and press method. So. sample SR-Ivocap resin cured by continuous pressure injection method seems to be superior to sample QC-20 resin cured by pack and press method in impact strength.