Traditionally, many kinds of mechanical bonding techniques were used for bonding resins to the surface of the metal alloys. If there is a seperation between resin and metal junction by stress accumulation and temperature change of oral cavity, the cracks or crazing may occur, accompanied by failure of resin bonding to metal. This study was designed to compare the shear bond strength of the type IV gold alloy and Cr-Co alloy surfaces treated with various methods and thermocycling. Universal Instron (Model 1000) and scanning electron microscope (JEOL, Japan) was used to record the shear bond strength of 5 groups. Forty specimens were made for each group ; group 1 was treated with sandblasting only, group 2 was coated with V-primer after sandblasting, group 3 was coated with Metal primer, group 4 wase coated with MR Bond and group 5 was coated with silane. After treated with various methods, thermocycling was done for half of the each group. The surfaces of failed pattern were observed with SEM. The results were as follows : 1. Shear bond strength of the group 1 was lower than that of another groups in type IV gold alloys and bond strength of the group 1, 2 were lower than that of group 3, 4, 5 in Cr-Co alloys. 2. Shear bond strength of the gold alloy with resin was higher than that of Cr-Co alloy when specimens were coated with V-primer. 3. Shear bond strength of the Co-Cr alloys with resin was higher than that of gold alloys when specimens were coated with Metal primer. 4. The bond strength of all specimens did not decreased significantly after thermocycling. 5. Adhesive failures were found in group 1 and Cr-Co alloy in group 2, but adhesive and cohesive failures were found in another groups.