The purpose of this study was to compare the marginal fit of all ceramic crowns prepared from alumina slip casting, which is consistent with the conventional In-ceram system, and those fabricated from alumina tapes which is currently under development in an effort to alleviate complexities involved in the forming procedure of the In-ceram crown core. All ceramic crowns, made of In-ceram(slip casting) and alumina tapes(Doctor blade casting), were prepared with $90^{circ};and;135^{circ}$ shoulder margins. The crowns were cemented with a glass ionomer cement and embeded in epoxy resin. The embedded crowns were sectioned faciolingually and mesiodistally and marginal discrepancies and marginal gaps were measured under the Measurescope MM II. The measurements were analyzed using Wilcoxon rank sum test and Kruskal-Wallis test and the results were as follows: 1. In the case of $90^{circ}$ shoulder margin, the combined marginal discrepancies and marginal gaps were $78.3{mu}m;and;44.4{mu}m$ respectively, for the all ceramic crowns fabricated using the alumina tapes. In comparison, the values were $65{mu}m;and;25.5{mu}m$ for the In-ceram crowns. For the marginal gaps a statistical difference existed (p<0.05) but no significant difference was observed for the marginal discrepancy (p>0.05). 2. In the case of $135^{circ}$ shoulder margin, the combined marginal discrepancy and marginal gaps were $82.1{mu}m;and;40.2{mu}m$ respectively, for the all ceramic crowns formed with the tapes. As compared with the marginal discrepancy and gaps of the $90^{circ}$ shoulder margin in the fabricated from the alumina tapes, no significant statistical differencies were discerned in both cases (p>0.05). 3. There was no statistically significant difference in the fits among four locations around the margins of the all ceramic crowns fabricated using the alumina tapes. The results obtained in this study showed that the marginal fits of the glass infiltrated alumina cores fabricated from the alumina tapes are slightly higher value than those prepared using the In-ceram but the difference is within a clinically acceptable range.