The physical properties of polymer are greatly influenced by the extent to which a resin cures. The presence of un reacted monomer can, have a plasticizing effect on the polymer, thereby altering the physical and mechanical properties of dentin bonding agent (DBA). If the DBA does not polymerize sufficiently, it will leave a weak bonding layer and lead to lower bond strength. The purpose of this study was to evaluate the shear bond strengths(SBS) and the degree of conversion (DC) of 4 commercialy avilable dentin bonding systems which are composed of 2 multi-bottle systems [Scotchbond Multi-Purpose (SMP), AeliteBond(AB)] and 2 onebottle systems [SingleBond(SB), One-Step(OS)]. For shear bond strength measurement, labial surfaces of freshly extracted bovine incisors were ground with # 600 grit SiC paper to expose dentin. Four different groups of samples were formed, with 10 samples. being made for each of the 4 commercial DBA in each group according to the curing sequences of DBA and overlayer thickness of composites: Group I (standard cure and 1mm thick composites) : The DBA was light cured and the composites of 1mm thickness was applied ; Group II (standard cure and 2mm thick composites) : The DBA was light cured and the composites of 2mm thickness was applied; Group III (simultaneous cure and 1mm thick composites) : The DBA was not light-cured and simultaneously cured with composites of 1mm thickness; Group N (simultaneous cure and 2mm thick composites) : The DBA was. not light-cured and simultaneously cured with composites of 2mm thickness. The SBS was measured immediately after the composites was bonded to the bovine dentin using an Instron machine. The DC of the DBA was examined in a thin film under simulated conditions of the experimental groups according to the curing sequences and overlayer thickness of composites in the SBS test. using a Fourier transform Infrared(FTIR) spectrometer. The following results were obtained from SBS tests and DC measurements 1. In SBS tests, the multi-bottle DBA(SMP, AB) had a generally higher bond strength values than the one bottle DBA(SB, OS). In DC measurements, the one bottle DBA(SB, OS) had a significantly higher DC than the multi-bottle DBA(SMP, AB). 2. In all DBAs except OS, there was no significant difference between the bond strength of group I (standard cure and 1mm thick composites) and that of group III (simultaneous cure and 1mm thick composites). SMP, SB in Group I had a significantly higher DC than those in group III, but AB, OS in group I had a significantly lower DC than those in group III 3. All DBAs in Goup II (standard cure and 2mm thick composites) had significantly higher bond strength and DC than those in Group N (simultaneous cure and 2mm thick composites). 4. In all DBAs, there was no significantly different SBS and DC between Group I and Group II, but all DBAs in Group III had significantly higher SBS and DC than those in Group IV.