The purpose of this study was to observe the morphologic change of dentinal surface, adhesion in interface between dentin and bonding agents, and penetration pattern of resin tags into dentinal tubles according to bonding procedure of ONE-STEP universal adhesive system. Ten extracted human molars were mounted in dental stone and sectioned to expose mid-coronal occlusal dentin and again sectioned tooth crown apically. Specimens were randomly assigned to three groups for dentin conditioning with 32% phoshoric acid, two coats of bonding agents after dentin conditioning, and bond of composite resin. The surfaces of dentin were treated with etch ant and applied bonding agent, and bonded composite resin according to the directions of manufacturer. Specimens which were boned composite were sectioned longitudinally for observing interfaces between resin and dentin. Two of specimens which were sectioned longitudinally were immersed in 6 N HCL for 30 seconds and 1% NaOCL for 12 hours to partially demineralize and deproteinize the dentin substrate. Each specimen was mounted on a brass stub, sputter-coated with gold and observed under SEM. The result were as follows : 1. On the dentinal surface which was conditioned with 32% phosphoric acid. the smear layer was completely removed. orifices of dentinal tubules were opened 3-$5{mu}m$ wide. and dentinal surface was irregular. 2. On the dentinal surface which was applied ONE-STEP. bonding agent. resin particles were observed on the orifices of dentinal tubules and intertubular dentin. 3. There were close adaptation between dentin and resin and were the pattern which composite invaded into dentin. 4. 1-$3{mu}m$-wide hybrid layer was visible in the interface between dentin and resin. 5. Long and funnel shaped resin tags were observed in demineralized specimens. and the surfaces of tags were rough.