The purpose of this study is to evaluate the castability and surface roughness of the casts using Non-percious alloys. For samples of 25 wax patterns, it is made from eight layers of sheet wax, arranged in the escalating layers. After fabricated wax patterns, using 5 kinds of Ni-Cr alloys is casted, and the casts are sandblasted. To castability, magnifier is used and values of surface roughness of the casts is measured with profilometer(tracing length 1.75mm, cutoff value 0.25mm) The results are as follows : 1. The castanbility of alloys, in case of C alloys, showed with $8.0{pm}0.0000$, and in case of CS alloys and N alloys showed equal with $7.8{pm}0.4472$, respectively. T alloys and V alloys showed equal with $7.2{pm}0.4472$, respectively. 2. The values of surface roughness of the casts are decreased more T alloys than in case of order alloys, and in order, increased in case of CS alloys, C alloys, V alloys, N alloys, respectively.