This study investigated the corrosion rate of aluminum in alkaline solution. It was performed to observe the effects of alloy element, alkalinity (KOH concentration), solution temperature, and inhibitor and its concentration in the solution. Among species of aluminum, AA-1050 showed the lowest corrosion rate due to its high purity $(>199\%)$, whereas alloys containing Mg anuor Mn were highly corroded, relatively. The corrosion rate could be reduced over than $50\%$ by saturating the solution with ZnO, while ZnAc did not work as an inhibitor. The inhibition effect of ZnO increased with increasing the alkalinity and solution temperature. It was found that the corrosion rate linearly increased with the concentration of KOH in first order and exponentially decreased with the inverse of the solution temperature. An analysis of the corroded material covered the surface of aluminum was made by SEM and EDS. According to the analytical results by using XRD, it was confirmed that $Al(OH)_3$ was produced from the corrosion of aluminum in KOH solution.