The changes on microstucture of recombinated gels with different ratio of amylose(A) and amylopectin(AP) which were isolated from nonwaxy rice starch were investigated by scanning electron microscope(SEM) and X-ray diffractometer. As the concentration of amylose was above 3%(1.08% of soluble amylose) in the amylose suspension, gel matrix became like a three-dimensional network. The microstructure of amylose gels showed a network including macroporous structure, but the higher the ratio of amylopectin content were, the firmer network were formed. In case of A/AP mixed gels(15%) with different amylose/amylopectin percent ratios ; 0/5, 5/10, 10/5, 15/0%, as the storage time of gels and the percent ratio of amylose content were increased, network was formed harder with thick films. While X-ray diffractograms of waxy rice starch which contained 100% amylopectin showed A type, those of purified amylose and amylopectin showed V type and amorphous patterns, respectively. Amylose(3%) gels added $2{sim}3%$ amylopectin and A/AP mixed gels(15%) showed peak at $2{ heta};=;17.0^{circ}$which were shown B type crystallinity similar af retrograded starches. Also as the percent ratio of amylose content in mixed gels was increased, peak intensity wat increased.