Fracture toughness({TEX}$J_{IC}${/TEX}) on 304 austenitic stainless steel weldments artificially degraded for long period under SCC environments were evaluated to investigate its reliability and environmental characteristics. Electro-chemical polarization tests were previously carried out to evaluate corrosion susceptiblility of weldment, and stress corrosion cracking was tested under various conditions of 3.5wt.% NaCl solution, the temperature of $25^{circ}$C and $95^{circ}$C</TEX>, and oxygen concentration during 3000hours. From the results obtained, it was found that 304 stainless steel weldment was so susceptible under high temperature and high oxygen concentration of 3.5wt.% NaCl solution, and fracture toughness({TEX}$J_{IC}${/TEX}) was also considerably reduced by material degradation.