Four organic polymers were mixed with mothmorillonite. Two cationic polymers a hi로 molecular weight polyacrylamide (494C) and a low molecular weight polymer (587C).Two anionic polymers include a high molecular weight polymer (aerotil). Each clay supension series were allowed to stand for 24 hours and were centrifuged, and the clay plugs were washed and dried. The dried samples investigated by XRD, IR and CEC measurement. The suspended clay containing anionic polymers was not flocculated at any concentratuons of polymer. But the suspendions containing two cationic polymers were rapidly flocculated at almost all concentrations. the d(001) spacings of Na-montmorillonite after being with cationic polymer 587C show about 15$AA$ suggesting the polymers may have entered the interlayer spaces. The polymer 494C-treated sample produced double peaks of about 12 and 15$AA$ in XRD. It indicates that the high molecular weight polymer. And cationic polymer 494C may be adsorbed mainy on the outside surface of clay, and some polymers may peretrate into olny interlayers in the margin of montmorillonite particles because of its high molecular weught. CEC of polumer 587-treated sample was reduecd mmarkedly suggesting polymer blocks CEC sites. The d(001) spacings of Ca-montmorillonite after being treated with cationic polymers show about 15$AA$ suggesting that the interlayer spaces have not been expanded. In the experiment using a dilute Ca-bearing solution, the suspended caly containinf anionic polymers was flocculated. The results indicate that the flocculation behavior of montmorillonite-polymer supension depends on not only polymer properties such as concentration, electric charge and molecular weight but also compositions of solvent.