Effects of surface conditions (temperature and roughness) of test specimens, when measuring emissive power of far-infrared ray, have been investigated using FT-IR spectrometer. Element metal zinc (Zn) was selected in this study as representative specimen of materials consisting of simple element. The zinc specimens were heated to four temperatures, i.e., 333K, 353K, .373K, and also their surface was finished with SiC abrasive papers of 100, 220, 360, 400, 600, 800, and 1000 mesh in size. The results shows that the emissive power (W/㎡) of the far-infrared ray increases with temperature for a given roughness and its relationship may be expressed by the following equations: Yη=1.0=0.142$.$T-0.937 for η=1.0, and Yη=10=0.016$.$T-1.286 for η=10. The emissive power is also known to increase with surface roughness for a given temperature. Their relationship can be represented by the following equations: YT=313K=0.234$.$$ell$n(η)+3.53, at 313K, YT=353K=0.234$.$$ell$n(η)+4.02 at 353K and YT=393K=0.243$.$$ell$n(η)+4.62 at 393K.