The activity of domestic pigment titania$(TiO_2)$ impregnated with vanadia$(V_2O_5)$ was investigated in the laboratory microreactor. The meta-titanic acid$(TiO(OH)_2)$ which was produced at Hankook Titanium was selected as the precursor for support. The domestic pigment $TiO_2$ showed higher activity in the reduction of NO with $NH_3$ than the foreign commercial $TiO_2$. $WO_3$ were added to domestic $V_2O_5/TiO_2$ catalytic system to improve the catalytic activity at higher reaction temperature between 400~50$0^{circ}C$ Also, the deactivation of domestic $V_2O_5/TiO_2$ and $WO_3-V_2O_5/TiO_2$ catalyst by $SO_2$ and $H_2O$ was investigated.