The 9 $mu extrm{m}$ GaN films on sapphire substrate were grown by Hydride vapor phase epitaxy. Dislocation density of these GaN films was measured by TEM. GaN film with crack free and mirror surface was directly grown on sapphire substrate. The dislocation density of this GaN film was $2{ imes}10^9/cm^2$. The surface of GaN film on patterned GaN layer also presented a smooth mirror. But a part of GaN surface included holes because of incomplete coalescence. The dislocation density of GaN film above the mask region was lower than that in the window region. Especially, the dislocation density in the region between mask center and window region was close to dislocation free. The average dislocation density of ELO GaN was $8{ imes}10^7/cm^2$.