Erbium (Er) doped $LiNbO_{3}(Er:LiNbO_{3})$ single crystal fibers were grown free of creacks along the c-axis by micro-pulling down method. The $Er^{3+}$ concentration was distributed homogeneously along the growth axis. The samples for optical characterization were cut from as-grown single crystal fibers and polished. When the 980nm light was incident on the sample, upconversion phenomena were observed at the green range of wavelength 510~570nm. In addition, the intensity of upconversion was remarkably increased by increasing the concentration of $Er_{2}O_{3}$ dopant in as-grown $Er:LiNbO_{3}$ crystals.