For 6H-SiC crystals which was obtained by sublimation growth, the formation of micropipes and internal planar defects was discussed in consideration of the inter-relationship between mass adsorption behavior and the defects origin on the growth interface on the basis of KSV theory and the the step growth pattern on the vicinal plane. Micropipes and planar defects was formed in the region which the step could not be grown by impurities impinging. It was realized that the internal defects formation was related to the crystallographic step planes formed on the growth interface and the migration of the molecules adsorbed on it.