The formation of $n-TiO_2$ powder by oxidation of Ti-ethoxied vapor in a flat flame burner reactor maintained under 20 torr has been studied. The produced powder were characterized in terms of crystal structure, chemical composition by XRD and TEM. The results showed that the powder consisted of loose agglomerated anatase and rutile particles and their size were about 10 nm and 20 nm, respectively. In the course of synthesis, changes of the flame color were happened to each condition during heating up the bubbler. The flame color transition phenomena reveled that a critical precursor delivery rate was needed for the powder formation (obtainable powder yield). The critical precursor delivery rate was estimated by a simple function of the bubbler temperature and the carrier gas flow rate. The critical precursor delivery rate was reviewed as an important variable of the nanopowder synthesis.