The effect of aliovalent dopents, $Nb_3O_5$ and MnO, on the grain growth kinetics of 12 mol% ceria stabilized tetragonal zirconia polycrystals (Ce-TZP) was studied. All specimens were sintered at $1550^{circ}C$ for 20 minutes prior to annealing at different temperatures to study grain growth kinetics. Grain growth kinetics of Ce-TZP and 1 mol% $Nb_2O_5$ doped Ce-TZP (Ce-TZP/$Nb_3O_5$) during annealing at 1475, 1550, and $1600^{circ}C$ adequately matched with square law $(D^2-D_;o^2=k_at)$. However, grain growth in 1 mol% MnO suppressed grain growth in Ce-TZP by drag force exerted by $Mn^{+2}$ ions which segregated strongly to the positively-charged grain boundaries of Ce-TZP, $Nb_2O_5$ enhanced grain growth by increasing the concentration of vacancies of $Zr^{+4}$ ion and $Ce^{+4}$ ions. Surface analysis with X-ray photoelectron spectroscopy (XPS) showed the segregation of Mn+2 ions to grain boundaries. The kinetics of grain growth obtained in the base Ce-TZP and the Ce-TZPs with the aliovalent dopants were examined in the context of impurity drag effect and space charge effect.