Effect of the particle size of $MgTiO_3$ and $CaTiO_3$ on the microstructural evolution during sintering of $0.93MgTiO_3-0.07CaTiO_3$ system was investigated. Microwave dielectric characteristics of the sintered ceramics were also measured. The microstructural evolutions were explained with an emphasis on the entrapping behavior of $CaTiO_3$ grain into the $MgTiO_3$ grain and were correlated with microwave dielectric characteristics. With an increasing particle size ratio between $CaTiO_3$and $MgTiO_3$, the fraction of entraped $CaTiO_3$ grains increased, which grain growth of $MgTiO_3$were concurrently accelerated due to decreasing drag force of its boundary migration. Besides, $CaTiO_3$-grain entrapment into the $MgTiO_3$grain interior led to decreaseing quality factor values.