The compressibility sinterability sintering behaviour and thermal stability of AlOOH added UO2 pellt and PVA-Al(III) complex added UO2 pellet were investigated respectively. Compared with characteristics of AlOOH added UO2 pellet the green density and the sintered density of PVA-Al(III) complex added UO2 pellet were lowered but the grain size and the pore size of that were more increased in accordance with higher compacting pressure. The AlOOH added UO2 pellet had the grain size of about 14${mu}{ extrm}{m}$ with monomodal pore size distribution while the PVA-Al(III) complex added UO2 pellet had the grain size of about 42 ${mu}{ extrm}{m}$ with bimodal pore size distribution. The PVA-A(III) complex added UO2 pellet had a similiar open porosity to the AlOOH added UO2 pellet and a lower resintered density change than the AlOOH added UO2 pellet.