The Si3N4 composites reinforced with carbon-coated SiC whiskers were fabricated by hot-pressing at 180$0^{circ}C$ for 2 hours to examine the effects of carbon-coated whiskers on the mechanical properties of SiC whisker reinforced Si3N4 composites. The flexural strength of the Si3N4 composites and Si3N4 monolith respectively. The weak interfacial bond between carbon-coated SiC whiskers and Si3N4 matrix which enhances the crack deflection and whisker pull-out could contribute to the improvement of mechanical properties of the composites.