Densification behavior and microstructural evolution during the liquid-phase sintering of alumina-anorhite system were investigated as a function of MgO addition. When MgO component was added in either alumina or anorthite glass powder the aspect ratio of alumina grains decreased and concurrently the are of flat interface which was formed as a result of contact solid alumina gains rather increased. Consequently addition of MgO component in the Al2O3-amorthite system brought about suppression of the rearrangement of solid grains during the liquid phase sintering and then densification of specimens was also retarded.