Sintering characteristics and dielectric properties of low temperature sinterable Glass/Ceramic dielectric materials were investigated. The dielectric materials which were developed for microwave frequency applications consist of SiO2-TiO2-Bi2O3-RO system(RO:BaO-CaO-SrO) crystallizable glass and Al2O3 as a ceramic filler. Sintering experiments showed that no more densification occurred above 80$0^{circ}C$ and bulk density and shrinkage depended on Al2O3 content only. Results of dielectric measurements showed that $varepsilon$r Q$ imes$f and $ au$f of the material containing 30wt% Al2O3 were 17.3, 600 and +23 ppm respectively. Those values for 45 and 60wt% Al2O3 samples were 11.6, 1400, +0.7 ppm and 7.2, 2000, -8.5 ppm, repectively. The results clearly showed that the Glas/Ceramic materials of present experiment decreased in $varepsilon$r and increased in $ imes$f value and changed from positive to negative value in $ au$f value with the increasement of Al2O3 content.