Polyaniline(PAn)-nylon 6 composite fabrics were prepared by immersing the nylon 6 fabrics in 100% distilled aniline for specified diffusion time and drawn out. Then the excess aniline on the fabric surface was blotted and successive polymerization was initiate by immersing them into oxidant and dopant solution for in situ polymerization of polyaniline. Consequently highly conductive PAn-nylon 6 composite fabrics could be obtained and the conductivity reaches as high as 10-2 S/cm. The maximum conductivity was obtained when the fabric was immersed in 100% aniline at 4$0^{circ}C$ for 3hours and polymerization was proceeded in 0.25M ammonium peroxydisulfate solution at 5$^{circ}C$ for 1hour.