The magnetic properties between Mn-Ir antiferromagnetic layer and Ni-Fe ferromagnetic layer have been investigated in Mn-Ir/Ni-Fe/Zr on Si wafer formed by magnetron sputtering. Mn-Ir was sputtered from Ir chips and Mn target using D.C. power, Ni-Fe and Zr were deposited from Ni-Fe and Zr targets using D.C. power under Ar atmosphere. We studied the dependence of the magnetic properties on Ir content of Mn-Ir layer for Mn-Ir/Ni-Fe bilayer, and obtained the highest $H_ex$ of 219 Oe and the low $H_c$ of 30 Oe. And then focused on the effect of base pressure for Mn-Ir containing multilayers. Our experimental data showed that if the base pressure is higher than $3.0{ imes}10^{-6};Torr$, the exchange anisotropy of Mn-Ir/Ni-Fe/Zr disappeared probably due to the grain refining of Mn-Ir film. In addition we have studied the dependence of Zr buffer on magnetic properties of Mn-Ir/Ni-Fe/Zr multilayers, and observed that Zr buffer about (111) texture and lower $H_c$ of Mn-Ir/Ni-Fe/Zr multilayer.