Bi-doped lanthanum magnetics $(La_{0.67-x}Bi_xCa_{0.33}MnO_3(x;=;0,; 0.04,; 0.1,; 0.2))$ samples have been prepared by standard ceramic process. The crystallinity and microstructures of the samples have been investigated by x-ray diffractometry and optical microscopy, respectively. The magnetic and magnetoresistive properties of the samples have been measured by vibrating sample magnetometery and van der Pauw method, respectively, at the temperatures ranging of 100 K~300 K with applied magnetic field of 0.4~0.5 T. Good crystallinity and high Curie temperature (275 K) have been obtained for the Bi-doped samples with small dosage (x = 0.04, 0.1) even they were sintered at 120$0^{circ}C$, which is about 20$0^{circ}C$ lower than normal sintering temperature of 140$0^{circ}C$. The Bi-doped samples with the small dosage showed lower relative electrical resistivity and higher magneto-resistive ratio compared to the undoped sample in the most temperatures measured. The Bi-doped samples also exhibited large magnetoresisitve ratio (maximum of 15% for x = 0.1) at room temperature even under a weak magnetic field of 0.4 T.