The effect of different plasma surface preparation and oxidation processes for the formation of $SiO_2-Si$(100) interfaces was studied using angle resolved uv-photoelectron spectroscopy. The surface preparation processes included ex situ preclean as well as in situ hydrogen plasma, which were compared to the processes of UHV annealing at high temperature. The spectral position of the oxide valence band features, with respect to the Fermi level. Were found to shift according to the different processes of surface preparation and oxidation. The shifts were analyzed in terms of band bending in the Si. Origins of the spectral shifts were considered to include defects at the $SiO_2Si$ interfaces and surface morphology(roughness) dependent on the surface preparation processes. From comparison of the ARUPS results of the various processes, it was concluded that the interface bonding of the silicon oxide-showed the lowest band bending.