For large scale applications of high temperature superconductor (HTS) such as transmission cables, motors and generators, long length of flexible HTS conductor is required. Currently, Bi-2223 HTS tape is capable of being fabricated in longer than 100 m length by industrial processes. In this study, we fabricated 100 m 19 filamentary Bi-2223 ($Bi_{1.8}Pb_{0.4}Sr_2Ca_2O_{10+x}$) HTS tape by PIT (Power in Tube) process. Critical current(IC) of this long length tape was measured 18.5 A at 77K, self field. Critical current of 100 m length tape was mainly resulted from the increase of inhomogeneity in oxide from the increase of inhomogeneity in oxide layer. Engineering critical current (Je=Ic/total tape cross-section area) that is important factor for practical applications and fabrication cost was measured 2.2 kA/cm2.